Zavojnica od nehrđajućeg čelika 410S
Opis
Tehnički podaci:
1. Standard: ASTM A240, JIS G4304, EN10088
2. Ocjena: 200serija&300serija&400serija
3. Debljina: 0,03 mm - 6,0 mm
4. Širina: 8mm-600mm
5. Duljina: prema zahtjevu kupaca
6. Površina: 2D, 2B, BA, Mirror finished, N04, Hair Line, Matt finish, 6K, 8K
7.Tehnologija: hladno vučeno/hladno valjano/vruće valjano
Materijali:
| Tip | Razred | Razred | Kemijska komponenta % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | ostalo | |||
| Austenitni | 201 | SUS201 | ≤0,15 | 16.00-18.00 sati | 3.50-5.50 | 5,50-7,50 | ≤0,060 | ≤0,030 | - | ≤1,00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17.00-19.00 sati | 4.00-6.00 sati | 7.50-10.00 sati | ≤0,060 | ≤0,030 | ≤1,00 | - | ≤0,25 | － | ||
| 301 | 1.4310 | ≤0,15 | 16.00-18.00 sati | 6.00-8.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | ≤0,10 | - | |
| 304 | 1.4301 | ≤0,07 | 17.00-19.00 sati | 8.00-10.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304L | 1.4307 | ≤0,030 | 18.00-20.00 sati | 8.00-10.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304H | 1,4948 | 0,04-0,10 | 18.00-20.00 sati | 8.00-10.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309 | 1.4828 | ≤0,20 | 22.00-24.00 sata | 12.00-15.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309S | * | ≤0,08 | 22.00-24.00 sata | 12.00-15.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 310 | 1,4842 | ≤0,25 | 24.00-26.00 sati | 19.00-22.00 sata | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24.00-26.00 sati | 19.00-22.00 sata | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1,4841 | ≤0,25 | 23.00-26.00 sati | 19.00-22.00 sata | ≤2,00 | ≤0,045 | ≤0,030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1.4401 | ≤0,08 | 16.00-18.50 sati | 10.00-14.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | - | - | |
| 316L | 1.4404 | ≤0,030 | 16.00-18.00 sati | 10.00-14.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | - | - | |
| 316Ti | 1.4571 | ≤0,08 | 16.00-18.00 sati | 10.00-14.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | 0,1 | Ti5(C+N)~0,70 | |
| 317 | * | ≤0,08 | 18.00-20.00 sati | 11.00-15.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1,00 | - | 0,1 | - | |
| 317L | 1.4438 | ≤0,03 | 18.00-20.00 sati | 11.00-15.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1,00 | - | 0,1 | - | |
| 321 | 1,4541 | ≤0,08 | 17.00-19.00 sati | 9.00-12.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 321H | * | 0,04-0,10 | 17.00-19.00 sati | 9.00-12.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 347 | 1,4550 | ≤0,08 | 17.00-19.00 sati | 9.00-12.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb≥10*C%-1,10 | |
| 347H | 1.494 | 0,04-0,10 | 17.00-19.00 sati | 9.00-12.00 sati | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb≥10*C%-1,10 | |
| Duplex | 2205 | S32205 | ≤0,03 | 22.0-23.0 | 4,5-6,5 | ≤2,00 | ≤0,030 | ≤0,020 | 3,0-3,5 | ≤1,00 | - | 0,14-0,20 | |
| 2507 | S32750 | ≤0,03 | 24.0-26.0 | 6,0-8,0 | ≤1,20 | ≤0,035 | ≤0,020 | 3,0-5,0 | ≤0,80 | 0,5 | 0,24-0,32 | ||
| Ferit | 409 | S40900 | ≤0,03 | 10.50-11.70 sati | 0,5 | ≤1,00 | ≤0,040 | ≤0,020 | - | ≤1,00 | - | ≤0,030 | Ti6(C+N)~0,50 Nb:0,17 |
| 430 | 1Cr17 | ≤0,12 | 16.00-18.00 sati | - | ≤1,0 | ≤0,040 | ≤0,030 | - | ≤1,0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17.50-19.50 sati | 1 | ≤1,00 | ≤0,040 | ≤0,030 | 1,75-2,5 | ≤1,00 | - | 0,035 | Ti+Nb:0,2+4(C+N)~0,80 | |
| martenzit | 410 | 1Cr13 | 0,08-0,15 | 11.50-13.50 sati | 0,75 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 sati | 0.6 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 420 | 2Cr13 | ≥0,15 | 12.00-14.00 sati | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12.00-14.00 sati | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0,07 | 15.00-17.50 sati | 3.00-5.00 sati | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | 3.00-5.00 sati | - | Nb 0,15-0,45 |
| 631 | 17-7PH | ≤0,09 | 16.00-18.00 sati | 6.50-7.50 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | ≤0,50 | - | Al 0,75-1,50 | |
| 632 | 15-5PH | ≤0,09 | 14.00-16.00 sati | 3.50-5.50 | ≤1,00 | ≤0,040 | ≤0,030 | 2.00-3.00 | ≤1,00 | 2,5-4,5 | - | Al 0,75-1,50 | |
Osnovne informacije
Zavojnica od nehrđajućeg čelika 410s, s dobrom otpornošću na koroziju i obradivošću, čelik je opće namjene i čelik za rezne alate.410S je vrsta čelika koja može poboljšati otpornost na koroziju i sposobnost oblikovanja čelika 410. 410S je čelik visoke čvrstoće koji može dodatno poboljšati otpornost čelika 410 na koroziju.Koristi se za lopatice turbina i dijelove visoke temperature.
• Specifikacije: AISI 410s, ASTM 410s
• Završeci: Ba površina, 2b površina, br. 1 (bijela koža), 2D površina, br. 4 (matirano), HL (crtanje žice), 8K površina imaju izvrsnu kvalitetu površine
• Primjenjuju se tolerancije glodanja na debljinu i ravnost. Nazovite JM Steel ako trebate određene veličine ili smjer zrna.
410S Karakteristična tehnologija obrade
1D -- Površina ima diskontinuirani granularni oblik, također poznat kao površina magle.
Tehnologija obrade: vruće valjanje + žarenje, sačmarenje, luženje + hladno valjanje + žarenje, luženje.
2D - blago srebrnasto bijela boja.
Tehnologija obrade: vruće valjanje + žarenje, sačmarenje, luženje + hladno valjanje + žarenje, luženje.
2B -- Srebrno bijela s boljim sjajem i ravnošću od 2D površine.
Tehnologija obrade: vruće valjanje + žarenje, sačmarenje, luženje + hladno valjanje + luženje žarenjem + valjanje za kaljenje i popuštanje.
Ba - Izvrstan površinski sjaj, visoka refleksija, poput površine ogledala.
Tehnologija obrade: vruće valjanje + žarenje, sačmarenje, luženje + hladno valjanje + luženje žarenjem + poliranje površine + valjanje za kaljenje i popuštanje.
Br. 3 -- Dobar sjaj, površina grubog zrna.
Tehnologija obrade: poliranje i kaljenje valjanjem za 2D ili 2B sa 100~120 abrazivnim materijalima (JIS R6002).
Br. 4 -- Dobar sjaj, fine linije na površini.
Proces obrade: poliranje i kaljenje valjanjem za 2D ili 2B s 150~180 abrazivnim materijalima (JIS R6002).
HL -- Srebrno siva s pramenovima dlake.
Tehnologija obrade: 2D proizvodi ili 2B proizvodi s odgovarajućom granularnošću abrazivnih materijala za poliranje površine je kontinuirano abrazivno zrno.
OGLEDALO -- Zrcalno.
Tehnologija obrade: 2D proizvodi ili 2B proizvodi s odgovarajućom granularnošću brusnog materijala brušenje i poliranje do efekta zrcala.